High-cycle tensile-tensile fatigue performance of niobium alloy: Conventional vs wire-arc additive manufacturing

초록

This study explores the high-cycle fatigue (HCF) behavior of a niobium alloy, NbZr1, fabricated using wire-arc additive manufacturing (WAAM), and compares its fatigue strength to that of its powder metallurgy (PM)-produced counterpart. The analysis was conducted at three different stress levels, each characterized by a non-zero mean stress and a stress ratio of 0.1. The fatigue life under tensile-tensile fatigue loading ranged from 104 to 108 cycles for all tested samples. WAAM-produced NbZr1 exhibited a shorter average fatigue life compared to PMNbZr1. Examination of the fracture surfaces revealed consistent fracture morphology across all loading conditions in PM-NbZr1 samples, whereas WAAM-NbZr1 samples showed varied fracture behavior. Notably, the crack propagation regions in WAAM-NbZr1 exhibited contrasting behaviors under different loading conditions. While PM-NbZr1 demonstrated typical ductile failure with elongated dimples near the final fracture region, WAAMNbZr1 showed more pronounced cleavage crack growth, accompanied by void nucleation and coalescence along the ZrO2 particles during fatigue crack propagation. The interdendritic regions containing fine ZrO2 particles were identified as a key factor influencing crack propagation and final fracture location in WAAMNbZr1.

키워드